　　3 结论
　　
　　本文给出了一种采用快速阳极氧化法直接氧化金属钛片制备具有高长径比、超细管径TiO2 纳米管粉的方法。FESEM 和TEM 结果表明所制备的TiO2 纳米管表面光滑、结构完整，其外径约为20 nm，管壁厚度约为5 nm。实验结果发现热处理温度对TiO2 纳米管粉的形貌和晶体结构以及光催化活性有重要影响：热处理温度在550oC 下时TiO2 纳米管状形貌能够基本保持，热处理温度在700oC 时TiO2 纳米管粉原始的管状形貌坍塌破坏；当热处理温度从300oC 增加到700oC，TiO2 纳米管粉经历了从单一锐钛矿相到锐钛矿金红石混合相，最后从锐钛矿金红石混合相到单一金红石相，这样一个晶体结构转变的过程；光催化降解甲基橙水溶液测试表明，当处理温度在550oC 时TiO2 纳米管粉呈锐钛矿金红石混合相，具有最强的光催化活性。本文研究结果说明在研究TiO2 纳米管粉的光催化活性时，热处理温度是一个十分重要的因素。

中国网提供大量免费硕士,如有业务需求请咨询网站客服人员！
　　
　　[参考文献] (References)
　　[1] Fujihira M, Satoh Y and Osa T. Heterogeneous photocatalytic oxidation of aromatic compounds on TiO2 [J].Nature, 1981, 293: 206～208.
　　[2] Jessensky O, Muller F and Gosele U. Self-organized formation of hexagonal pore arrays in anodic alumina [J].Appl. Phys. Lett., 1998, 72(10): 1173～1175.
　　[3] Ashid R, Morikawa T and Ohwaki T et al. Visible-Light Photocatalysis in Nitrogen-Doped Titanium Oxides[J]. Science, 2001, 293: 269～271.
　　[4] Zhong P and Que W X. Highly ordered TiO2 nano-pore arrays fabricated from a novelpolymethylmethacrylate/polydimethylsiloxane soft template [J]. Nano-Micro Lett. 2012, 2(1): 1～5. Doi:10.5101/nml.v2i1.p1-5.
　　[5] Macak J M, Zlamal M and Krysa J et al. Self-organized TiO2 nanotube layers as highly efficientphotocatalysts [J]. Small, 2007, 3(2): 300～304. （科教范文网 lw.nseaC.Com编辑发布）
　　[6] Khan M A, Jung H T and Yang O B. Synthesis and characterization of ultrahigh crystalline TiO2 nanotubes[J]. J. Phys. Chem. B., 2006, 110(13): 6626～6630.
　　[7] Chen Y S, Crittenden J C and Hackney S et al. Preparation of a novel TiO2-based p-n junction nanotubephotocatalyst [J]. Environ. Sci. Technol. 2005, 39: 1201～1208.
　　[8] Pavasupreea S, Ngamsinlapasathiana S and Suzukia Y et al. Preparation and characterization of high surfacearea nanosheet titania with mesoporous structure [J]. Mater. Lett. 2007, 61(14-15): 2973～2977.
　　[9] Lai Y K, Zhuang H F and Sun L et al. Self-organized TiO2 nanotubes in mixed organic-inorganic electrolytesand their photoelectrochemical performance [J]. Electrochimica. Acta. 2012, 54(26): 6536～6542.
　　[10] Liu D and Yates M Z. Fabrication of size-tunable TiO2 tubes using rod-shaped calcite templates [J]. Langmuir,2007, 23(20): 10333～10341.
　　[11] Li Y, Guo M and Zhang M et al. Hydrothermal synthesis and characterization of TiO2 nanorod arrays on glasssubstrates [J]. Materials Research Bulletin, 2012, 44(6): 1232～1237.
　　[12] Coakley K M, Liu Y and McGehee M D et al. Infiltrating semiconducting polymers into self-assembledmesoporous titania films for photovoltaic applications [J]. Adv. Funct. Mater, 2003,13(4): 301～306.