桥面铺装典型病害成因及其防治措施

 摘要： 近年来伴随着高速公路的快速, 桥涵构造物的养护工作现已提到新的日程，如何有效的保证高速公路安全服务标准，及时快速的发现的高速公路出现的各种病害，也是我们当前面临的需要不断改进的课题。本文重点论述了沥青混凝土桥面铺装裂缝、车辙、坑槽典型病害成因，并结合工作实际提出相应的防治措施。
Abstract: In recent years, along with the rapid development of highway, the conservation work of bridge structures has been referred to a new conservation agenda. How to effectively ensure the service standards of expressway safety and find emerging diseases in time is the issue we are facing and need to continually improve. This paper focuses on the causes of typical disease in the asphalt concrete pavement, such as cracks, rutting, pits, and so on,  and proposes appropriate measures combining with the actual work.
关键词：高速公路；沥青混凝土桥面铺装；病害；成因及防治措施
Key words: expressway；asphalt concrete deck pavement；disease；causes and control measures

        0  引言
        高速公路桥梁的桥面铺装直接承受行车荷载、连体变形环境因素的作用，伴随着高速公路运营年限的增加、一些施工设计因素、超载车辆的行驶等因素也加快了桥涵病害的产生和发展，以至于桥面铺装出现了裂缝、车辙等病害，对发现的病害应该尽早进行控制，及时的根据工作具体情况进行相应的治理与防护，这样才能更好保证高速公路服务水平。
        1  桥面铺装病害成因分析
        1.1 裂缝成因  桥面铺装裂缝产生的原因较为复杂，一般有以下几种形式：第一种是干缩裂缝，其产生原因由于混凝土相对湿度引起，这种裂缝随着相对湿度的增加而减小；第二种是温度裂缝，其产生原因主要是低温缩裂，面层降温而收缩的趋势会受到下部桥面板约束而产生拉力，随着温度降低，收缩趋势进一步增强，导致拉应力超过了沥青混凝的抗拉强度，便产生了开裂，一般为横向裂缝，严重时发展为纵向裂缝；第三种是疲劳裂缝，其产生原因是桥面铺装在正常使用情况下，由于荷载的多次反复作用引起的铺装层开裂，这也是桥面铺装的主要破损类型。 （科教论文网 lw.nSeAc.com编辑发布）
        1.2 车辙成因  车辙的产生原因可归纳为重载的作用、渠化交通、和铺装材料的性质等等，高温更是产生车辙的重要因素。 
        1.3 坑槽成因  坑槽产生原因是多方面的，首先铺装层沥青混合料设计孔隙率偏大或者施工时出现离析、压实不足，导致孔隙率更大，铺装层在水或者冰冻作用下，沥青逐渐失去，与矿料的粘合力，从矿料表面脱落，在车辆的作用下沥青混凝土铺装层出现松散状态，以骨料从铺装层脱落形成坑槽；其次由于施工中沥青混合料加热温度过高，致使沥青老化失去粘结力，造成沥青从矿料表面脱落所致；其次桥面不平整，在行车和温度荷载的作用下，造成这些地方铺装层内产生局部应力集中，出现结构性的点损失，然后逐渐四周扩散，而形成坑槽。
        2  桥面铺装病害处置对策
        2.1 灌缝法  ①当前受设计水平、铺装材料和条件的制约，桥面铺装开裂具有不可避免性，针对裂缝修复一般采用灌缝法，缝宽在6mm以内的，宜将缝隙刷扫干净，并用压缩空气除去尘土后在用热沥青或者乳化沥青封堵；缝宽6mm以上的，应剔缝隙内杂物和松动的缝隙边缘，或者裂缝开槽后用压缩空气吹静，采用沙粒式或者细粒式热拌沥青混合料填充、捣实，并用烙铁封口，随即撒沙，扫匀，也可用乳化沥青混合料填封。②灌缝注意事项：一定要将缝隙清理干净，封灌饱满，一般选择末冬初气温降低后集中封灌一遍，其它季节发现一道处理一道，不允许裂缝存在。