穿漳涵洞水毁修复工程试验研究(1)

摘要：通过对穿漳涵洞水毁修复工程所用水泥、砂砾石骨料、钢筋、壤土等材料以及试验手段的控制，保证了该项工程的顺利完成。对试验样本进行数理统计综合分析后表明：试验结果均满足设计要求。

关键词：穿漳涵洞水毁修复工程 材料 试验 试验样本 数理统计 分析 设计

study on the repairing project of the culvert spoiled by flood

abstract: by the control of the amount of cement, sand-gravel aggregate, reinforcing steel, loamy soil and the means of experiment in the repairing project of the culvert passing zhang river spoiled by devastating flood, it has been completed auspiciously. it is proved that all of the results are satisfied the demand of project’s designs by all-around analyzing with the method of mathematical statistics to testing samples

key words: repairing project of the culvert passing zhang river spoiled by devastating flood，materials，experiment, testing samples, mathematical statistics, analyze, design

1 前言

东风渠穿漳涵洞位于邯郸市魏县野胡拐乡大王村东南约300 m的漳河上，距上游的岳城水库约82 km。涵洞自南向北穿越漳河，为东风渠的主要工程，其主要作用是输水灌溉。穿漳涵洞原设计等级为ⅲ级，过水能力为50 m3/s，涵洞采用双排布置，内径4.0 m，为现浇钢筋混凝土无压涵洞，共28节，每节12.5 m，总长350 m。本次穿漳涵洞水毁修复工程设计等级仍为ⅲ级，主要将下游侧“96.8”洪水冲毁的6节涵管修复，设计输水能力为25 m3/s，内径3.9 m。未冲毁部分，在管内喷水泥砂浆补强处理。

2 材料组成

2.1水泥.

河北太行集团生产的太行山425#普通硅酸盐水泥和425#矿渣硅酸盐水泥，其物理性能见表1、表2[5]。由表1、表2可知，太行山425#普通硅酸盐水泥和425#矿渣硅酸盐水泥的物理性能均满足国家标准gb175－92的技术要求。

2.2砂石骨料

当地河砂与人工碎石，其物理性能检测结果见表3、表4[5]。

2.3钢筋。

新兴铸管公司(2672工厂)生产热轧圆钢、热轧带肋钢筋，其机械性能见表5[5]。

2.4壤土

其主要理性能见表6[1] [2] [3] 。

2.5外加剂

石家庄市长安育才建材厂生产的gk-5a高效减水剂、gk-9引气剂、gk-3a速凝剂。gk-5a高效减水剂的最佳掺量为水泥重量的0.6~0.8%；gk-3a速凝剂的最佳掺量为水泥重量的4~6%；gk-9引气剂的最佳掺量为水泥重量的0.01%。

共2页: 1